紅外透射可見吸收玻璃
作者：紅外透射可見吸收玻璃 日期：2010年04月03日
|
|
|
牌 號
|
厚度
(mm)
|
A[2856k]
|
D65
|
化學穩定性
|
ND
|
α×10-7
(/℃)
|
Tg
(℃)
|
Ts
(℃)
|
S
|
|
x
|
y
|
Y
|
x
|
y
|
Y
|
DA
|
DW
|
|
HWB760
|
3
|
|
|
|
|
|
|
5
|
4
|
1.532
|
111
|
534
|
592
|
2.77
|
|
HWB780
|
3
|
|
|
|
|
|
|
5
|
4
|
1.532
|
111
|
534
|
592
|
2.77
|
|
HWB800
|
3
|
|
|
|
|
|
|
5
|
4
|
1.520
|
98
|
559
|
615
|
3.05
|
|
HWB830
|
3
|
|
|
|
|
|
|
5
|
4
|
1.520
|
98
|
559
|
615
|
3.05
|
|
HWB850
|
3
|
|
|
|
|
|
|
5
|
4
|
1.520
|
98
|
559
|
615
|
3.05
|
|
| |
|
| 紅外透射可見吸收玻璃技術要求 |
紅外透射可見吸收玻璃氣泡、條紋、應力類級別 |
|
牌 號
|
厚 度(mm)
|
λtj
(nm)
|
λ0
(nm)
|
Tλ0
(%)
|
K
|
|
HWB760
|
3
|
760±10
|
850
|
≥83.6
|
≥0.6
|
|
HWB780
|
3
|
780±10
|
900
|
≥83.6
|
≥0.5
|
|
HWB800
|
3
|
800±10
|
900
|
≥83.6
|
≥0.5
|
|
HWB830
|
3
|
830±10
|
930
|
≥83.6
|
≥0.5
|
|
HWB850
|
3
|
850±10
|
950
|
≥80.0
|
≥0.5
|
|
|
牌 號
|
氣 泡
|
條 紋
|
應 力
|
|
HWB760
|
C-B
|
3C
|
3
|
|
HWB780
|
C-B
|
3C
|
3
|
|
HWB800
|
C-B
|
3C
|
3
|
|
HWB830
|
C-B
|
3C
|
3
|
|
HWB850
|
C-B
|
3C
|
3
|
|
| |
|
 |
| |
| |
|
|
B.紅外透射可見吸收玻璃特性
|
|
牌 號
|
厚度
(mm)
|
A[2856k]
|
D65
|
化學穩定性
|
ND
|
α×10-7
(/℃)
|
Tg
(℃)
|
Ts
(℃)
|
S
|
|
x
|
y
|
Y
|
x
|
y
|
Y
|
DA
|
DW
|
|
HWB900
|
6
|
|
|
|
|
|
|
3
|
3
|
|
|
|
|
2.57
|
|
HWB930
|
6
|
|
|
|
|
|
|
3
|
3
|
|
|
|
|
2.57
|
|
|
|
|
| 紅外透射可見吸收玻璃技術要求 |
紅外透射可見吸收玻璃氣泡、條紋、應力類級別 |
|
牌 號
|
厚 度(mm)
|
λtj
(nm)
|
λ0
(nm)
|
Tλ0
(%)
|
QZ(%)
|
|
HWB900
|
6
|
900±15
|
1050
|
≥80.0
|
≥0.2
|
|
HWB930
|
6
|
930±15
|
1050
|
≥80.0
|
≥0.2
|
|
|
牌 號
|
氣 泡
|
條 紋
|
應 力
|
|
HWB900
|
C
|
3C
|
3
|
|
HWB930
|
C
|
3C
|
3
|
|
|
* 為極少生產的玻璃牌號，洽商定購。
|
|
| |
|
 |
|